Note: The new F3125 specification is a consolidation and replacement of six ASTM standards, including; A325, A325M, A490, A490M, F1852, and F2280. Until the F3125 specification is more widely used and until the A325 and A490 specifications have been eliminated by ASTM, we will continue to sell A325 and A490 heavy hex structural bolts under their existing specification requirements, unless F3125 is referenced in the inquiry and/or purchase order.

The ASTM A325 specification covers high strength heavy hex structural bolts from 1/2″ diameter through 1-1/2″ diameter. These bolts are intended for use in structural connections and therefore have shorter thread lengths than standard hex bolts. Refer to the Structural Bolts page of our site for thread lengths and other related dimensions.

This specification is applicable to heavy hex structural bolts only. For bolts of other configurations and thread lengths with similar mechanical properties, see Specification A449.

Bolts for general applications, including anchor bolts, are covered by Specification A449. Also refer to Specification A449 for quenched and tempered steel bolts and studs with diameters greater than 1-1/2″ but with similar mechanical properties.

A325 Types

TYPE 1 Medium carbon, carbon boron, or medium carbon alloy steel.
TYPE 2 Withdrawn November 1991.
TYPE 3 Weathering steel.
T Fully threaded A325. (Restricted to 4 times the diameter in length)
M Metric A325.

A325 Connection Types

SC Slip critical connection.
N Bearing type connection with threads included in the shear plane.
X Bearing-type connection with threads excluded from the shear plane.

A325 Mechanical Properties

Size Tensile, ksi Yield, ksi Elong. %, min RA %, min
1/2 - 1 120 min 92 min 14 35
1-1/8 - 1-1/2 105 min 81 min 14 35

A325 Chemical Properties

Type 1 Bolts
Element Carbon Steel Carbon Boron Steel Alloy Steel Alloy Boron Steel
Carbon 0.30 - 0.52% 0.30 - 0.52% 0.30 - 0.52% 0.30 - 0.52%
Manganese, min 0.60% 0.60% 0.60% 0.60%
Phosphorus, max 0.040% 0.040% 0.035% 0.035%
Sulfur, max 0.050% 0.050% 0.040% 0.040%
Silicon 0.15-0.30% 0.10 - 0.30% 0.15 - 0.35% 0.15 - 0.35%
Boron 0.0005 - 0.003% 0.0005 - 0.003%
Alloying Elements * *
* Steel, as defined by the American Iron and Steel Institute, shall be considered to be alloy when the maximum range given for the content of alloying elements exceeds one of more of the following limits: Manganese, 1.65%, silicon, 0.60%, copper, 0.60%, or in which a definite range or a minimum quantity of any of the following elements is specified or required within the limits of the recognized field of constructional alloy steels: aluminum, chromium up to 3.99%, cobalt, columbium, molybdenum, nickel, titanium, tungsten, vanadium, zirconium or any other alloying elements added to obtain a desired alloying effect.